RTV2 condensation Liquid Silicone Rubber for Plaster Molds Making
DESCRIPATION
Silicone rubber MCSIL-2030 is a two-component material, consisting of Part A base and Part B MCSIL-CA30, cures at room temperature by a condensation reaction.
PRODUCT FEATURES
1. Good flow ability and long working time
2. Excellent performance for duplication
3. High tear and tensile strength
4. Easy de-mould from complex replica parts
5. Acid and alkali-resistance
6. Low linear shrinkage
APPLICATIONS
MC RTV-2 mold making silicone rubber are suited for casting a wide range of materials Polyester/ Polyurethane/ Epoxy resin, gysum/ plater, cemetns/ concrete , wax .
Technical Data
| Item No. | MCSIL-2030 |
| Color | White |
| Curing Agent | CA-30 |
| Mixing ratio | 100:2 |
| Mixed Viscosity | 25000cps |
| Working time | 30-40mins |
| Curing time | 6 hours |
| Hardness | 30±2 shore A |
| Tear Strength | 30 N/mm |
| Tensile Strength | 3.8Mpa |
| Shrinkage | ≤0.3% |
| Elongation | 520% |
USING INSTRUCTION
1- Take 100g of part A and add 2g of part B and mix the silicone rubber and curing agent evenly.
2- vacuum pumping
Without exception, this step takes less than 10 minutes. Otherwise, it will cause , and no more further steps will be available
3- Pouring mold or block mold of silicone rubber
The pouring way is an easy way to make molds, it's slowly and evenly pour into the mixed silicon rubber into the square frame. After the cross linking reaction.
Package
Part A base silicone: 5kg, 20kg/drum, 25kg/drum or 200kg/drum
Part B CA30 Curing Agent: 250g, 800g/bottle, 1kg/bottle
Certificates
Storage
When the silicone rubber is stored at or below 30 centi degree in the original unopened containers, Silicone Base and Curing agent have a usable life of 12 months from the date of production. After 12 months' stockpiles use the Stir to mix the Part A silicone for some minutes, then the silicone can be use again, no influence for other performance.